Steel Guide
Steel Guide – The Foundation of Every Knife
No knife without steel – the material at the very core of every blade.
What Is Steel?
Steel is an alloy in which iron is the primary component. By definition, its carbon content is generally less than 2%, and it contains other elements that significantly influence its properties. While exceptions exist, steel becomes hardenable starting at around 0.22% carbon content, making it essential for knife-making.
Why Alloying Elements Matter
The elements added to steel—such as chromium, vanadium, molybdenum, and others—have a major impact on hardness, corrosion resistance, edge retention, and toughness. Selecting the right steel is critical to ensuring a knife performs at the highest level.
Variety of Steels for Knife Blades
Today, the European Steel Register lists over 2,400 types of steel, each with unique characteristics. We’ve compiled a detailed table of the most common steels used in our knife blades, including their compositions and performance traits.
View the Steel Composition Table
| Name | Developed in | % Carbon | % Chrom | % Molybdenum | % Vanadium | % Mangan | % Nickel | % Silicium | % Cobalt | % Copper | % Phosphor | % Nitrogen | % Niobium | % Tungsten | HRC Hardness |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 1095 | USA | 0,9-1,03 | - | - | - | 0,3-0,5 | - | - | - | - | - | - | - | - | 56-59 |
| 12C27 | Sweden | 0,58 | 14 | - | - | 0,35 | - | 0,35 | - | - | - | - | - | - | 57-59 |
| 14C28N | Sweden | 0,62 | 14 | - | - | 0,6 | 0,2 | 0,03 | 0,11 | 57-59 | |||||
| 154CM | USA | 1,05 | 14 | 4 | 0,4 | - | 0,35 | - | - | - | - | - | - | 58-59 | |
| 3Cr13MoV | China | 0,26-0,4 | 12-14 | - | - | 1 | - | - | - | - | 0,04 | - | - | - | 52-55 |
| 4034 | Germany | 0,42-0,5 | 12,5-14,5 | - | - | 1 | - | 1 | - | - | - | - | - | - | 54-55 |
| 40X10C2M | Russia | 0,45 | 10 | 0,7-0,9 | 0,2 | 0,5-0,7 | 0,6 | 1,9-2,6 | - | 0,3 | 0,03 | - | - | - | 57-58 |
| 4116 | Germany | 0,45-0,55 | 14-15 | 0,5-0,8 | 0,1-0,2 | 0 | - | 0 | - | - | - | - | - | - | 55-56 |
| 420 | USA | 0,4-0,5 | 12-14 | - | - | - | - | - | - | - | - | - | - | - | 54 |
| 440A | USA | 0,6-0,75 | 16-18 | 0,75 | - | 1 | - | 1 | - | - | - | - | - | - | 56 |
| 440B | USA | 0,75-0,95 | 16-18 | 0,75 | - | 1 | - | 1 | - | - | - | - | - | - | 56 |
| 440C | USA | 0,95-1,2 | 16-18 | 0,75 | - | 1 | - | 1 | - | - | - | - | - | - | 58 |
| 5160 | USA | 0,56-0,64 | 0,7-0,9 | - | - | 0,75-1 | - | 0,15-0,3 | - | - | 0,04 | - | - | - | 56-59 |
| 5Cr15MoV | China | 0,45 | 15 | 0,5 | - | 1 | - | 1 | - | - | - | - | - | - | 55-56 |
| 8Cr13MoV | China | 0,8 | 13 | 0,15 | 0,1 | 0,4 | 0,2 | 0,5 | - | - | 0,02 | - | - | - | 58-60 |
| 95X18 | Russia | 0,9-1,1 | 17-19 | - | - | 0,8 | 0,6 | 0,8 | - | 0,3 | 0,03 | - | - | - | 57-58 |
| 9Cr18MoV | China | 0,9-1,05 | 16-19 | - | - | 0,8 | - | 0,8 | - | - | 0,03 | - | - | - | 56-58 |
| Acuto+ | Japan | 0,9-0,95 | 17-18 | 1,3-1,5 | 0,1-0,25 | 0,5 | - | 0,5 | - | - | 0,04 | - | - | - | 59-60 |
| AEB-L | Sweden | 0,67 | 13 | - | - | 0,6 | - | 0,4 | - | - | 0,025 | - | - | - | |
| ATS-34 | Japan | 1,05 | 14 | 4 | - | 0,4 | - | 0,35 | - | - | - | - | - | - | 58-59 |
| AUS-4 | Japan | 0,4-0,45 | 13-14,5 | - | - | 1 | 0,4 | 1 | - | - | 0,4 | - | - | - | 55-57 |
| AUS-6 (= 6A) | Japan | 0,55-0,65 | 13-14,5 | - | 0,1-0,25 | 1 | - | 1 | - | - | - | - | - | - | 56-57 |
| AUS-8 (= 8A) | Japan | 0,7-0,75 | 13-14,5 | 0,1-0,3 | 0,1-0,25 | 1 | - | 1 | - | - | - | - | - | - | 57-58 |
| C75 | Germany | 0,7-0,8 | - | - | - | 0,6-0,8 | - | 0,15-0,35 | - | - | 0,04 | - | - | - | 55-58 |
| CPM-10V | USA | 2,45 | 5,25 | 1,3 | 9,75 | 0,5 | 0,9 | 60-64 | |||||||
| CPM-3V | USA | 0,8 | 7,5 | 1,3 | 2,75 | 62-63 | |||||||||
| CPM-D2 | USA | 1,55 | 11,5 | 0,9 | 0,8 | - | - | - | - | - | - | - | - | - | 59-61 |
| CPM-M4 | USA | 1,4 | 4 | 5,25 | - | 0,3 | - | 0,55 | - | 0,06 | - | - | - | 5,5 | 60-62 |
| CPM-S-30V | USA | 1,45 | 14,5 | 2 | 4 | - | - | - | - | - | - | - | - | - | 58 |
| CPM-S-35VN | USA | 1,38 | 14 | 2 | 3 | 0,5 | - | 0,5 | - | - | - | 0,05 | 0,5 | - | 59-60 |
| CPM-S-60V | USA | 2,15 | 17,5 | 0,5 | 5,75 | 0,5 | - | 0,5 | - | - | - | - | - | - | 57-58 |
| CPM-154 | USA | 1,05 | 14 | 4 | - | 0,5 | - | 0,3 | - | - | - | - | - | - | 58-61 |
| Cronidur-30 | Germany | 0,25-0,35 | 14-16 | 0,85-1,1 | - | 0-1 | 0-0,5 | 0-1 | - | - | - | 0,3-0,5 | - | - | 58-60 |
| CTS 204P | USA | 1,9 | 20 | 1 | 4 | 0,3 | - | 0,6 | - | - | - | - | - | - | |
| CTS 20CP | USA | 2,2 | 13 | 1,3 | 9,3 | 0,5 | - | 0,9 | - | - | - | - | - | - | |
| CTS 40CP | USA | 1,7 | 18 | 1 | 3 | 0,3 | - | 0,8 | - | - | - | - | - | - | |
| CTS B52 | USA | 0,98-1,1 | 1,3-1,6 | - | - | 0,25-0,45 | - | 0,15-0,3 | - | - | - | - | - | - | |
| CTS B75P | USA | 1,1-1,2 | 14-15 | 3,8-4,2 | 1-1,5 | 0,5 | - | 0,3 | - | - | - | - | - | - | |
| CTS BD-1 | USA | 0,9 | 15,5 | 0,3 | 0,1 | 0,6 | - | 0,37 | - | - | - | - | - | - | |
| CTS BD-30P | USA | 1,5 | 14 | 2 | 4 | 0,5 | - | 0,3 | - | - | - | - | - | - | |
| CTS XHP | USA | 1,6 | 16 | 0,8 | 0,45 | 0,5 | 0,35 | 0,4 | - | - | - | - | - | - | |
| D2 | USA | 1,5 | 12 | 1 | 1 | 0,6 | 0,3 | 0,6 | - | - | - | - | - | - | 59-61 |
| Elmax | USA | 1,7 | 18 | 1 | 3 | 0,3 | - | 0,8 | - | - | - | - | - | - | |
| GIN-1 | Japan | 0,9 | 15,5 | 0,3 | - | 0,6 | - | 0,37 | - | 0,03 | 0,02 | - | - | - | 56-58 |
| H1 | Japan | 0,15 | 14-16 | 0,5-1,5 | - | 2 | 6-8 | 3-4,5 | - | - | 0,04 | 0,1 | - | - | 58-59 |
| Magnacut | USA | 1,15 | 10,7 | 2 | 4 | 0,5 | - | 0,4 | - | - | -0,2 | 2 | - | - | 61-62 |
| N690 | Austria | 1,07 | 17,3 | 1,1 | 0,1 | 0,4 | - | 0,4 | 1,5 | - | - | - | - | - | 58-60 |
| N695 | Austria | 0,95-1,2 | 16-18 | 0,75 | - | 1 | - | 1 | - | - | - | - | - | - | 57-58 |
| Niolox (1.4153) | Germany | 0,8 | 12,7 | 1,1 | 0,9 | 0,7 | 58-62 | ||||||||
| Nitro-B | Spain | 0,55 | 15,5 | 0,5 | 0,1 | 0,2 | - | 0,25 | - | - | - | 0,21 | - | - | 62 |
| Nitro-V | USA | 0,66-0,7 | 12,7-13,3 | - | 0,05-0,1 | 0,6-0,7 | - | 0,25 | - | - | - | 0-0,2 | - | - | 62 |
| RWL34 | Sweden | 1,05 | 14 | 4 | 0,2 | 0,5 | - | 0,5 | - | - | - | - | - | - | |
| S70 | USA | 0,45-0,55 | 3-3,5 | 1,3-1,8 | 0,2-0,3 | 0,2-0,8 | - | 0,2-1 | - | - | - | - | - | - | 60-62 |
| SGPS | Sweden | 1,4 | 15 | 2,8 | 2 | 0,4 | - | 0,5 | - | - | 0,03 | - | - | - | 62 |
| SK-5 | Japan | 0,9-1 | - | 0,3 | - | - | - | 0,3 | - | - | - | - | - | - | 57-60 |
| Sleipner | Sweden | 0,9 | 7,8 | 2,5 | 0,5 | 0,5 | 0,9 | >60 | |||||||
| T6MoV | France | 0,6 | 14,2 | 0,65 | 0,1 | - | 0,23 | - | - | - | - | - | - | - | 54-56 |
| VG-10 | Japan | 0,95-1,05 | 14,5-15,5 | 0,9-1,2 | 0,1-0,3 | 0,5 | - | 0,6 | 1,3-1,5 | - | 0,3 | - | - | - | 58-60 |
| VG-2 | Japan | 0,6-0,7 | 13-15 | 0,1-0,2 | - | 0,5 | 0,15 | 0,5 | - | - | 0,03 | - | - | - | 57-58 |
| X-15T.N. | France | 0,4 | 15,5 | 2 | 0,3 | - | - | - | - | - | - | 0,2 | - | - | 58 |
| X50CrMoV15 | Germany | 0,45-0,55 | 14-15 | 0,5-0,8 | 0,1-0,2 | 0 | - | 0 | - | - | - | - | - | - | 55-56 |
| ZDP-189 | Japan | 3 | 20 | - | - | - | - | - | - | - | - | - | - | - | 65-67 |
| Name | Developed in | % Carbon | % Chrom | % Molybdenum | % Vanadium | % Mangan | % Nickel | % Silicium | % Cobalt | % Copper | % Phosphor | % Nitrogen | % Niobium | % Tungsten | HRC Hardness |